Knowledge | Quartz Stone Easy To Crack-- Eight Locations And Reasons
- Oct 30, 2018 -

Many consumers have been blinded by the price of quartz stone countertops, thinking that the quality of quartz stone has little to do with price.


Just think that it can be used.


In fact, a penny of goods, high-end and low grade inferior quality is very different. 

Therefore, when consumers buy quartz stone countertops, it is recommended that you use high-

grade, large-scale quartz stone manufacturers to produce products.


The quality of quartz stone itself is on the one hand. In the process of processing and installation,

 if there is a situation in which the work is cut and the process is not strict, the cracking may occur

 in the later stage, such as the following:

shiyingshi

First, the crack at the joint of the countertop is cracked: the main installation workers are not

 aligned when the seam is seamed, and the top of the bell mouth is small and large, and the glue is 

not evenly coated. More importantly, the glue is not used after the glue is fixed, or Adding

 solidification in the glue or promoting the excessive amount of the seam to make the seam more

 brittle and slightly cracked during use;


Second, cracking at the corner: the wall is too tight and there is no shrinkage joint. The two cabinet

s are uneven or unflattened. The front corner is opened at right angles to form internal stress 

concentration, which is cracked by uneven impact or temperature change.


Third, the crack around the upper basin: no gap between the above counter basin and the basin hole,

 the basin hole is not polished smooth, the four corners of the basin hole are not rounded or left 

with a serrated print, and the table is not evenly cracked by external force impact or temperature

 change;


Fourth. Cracking around the furnace hole: no gap is left between the gas stove and the furnace hole

, the furnace hole is not polished smooth, the four corners of the basin hole are not rounded or 

left with serrated printing, and the surface is not uniformly cracked by external force impact 

or temperature change;

starlight-brown-quartz-stone-tiles副本

Fifth, the above counter basin, the front skirt of the furnace hole is cracked: the counter basin 

cabinet or the stove is placed flat, when the upper basin, the front skirt of the furnace hole is 

subjected to gravity (person stepping, stepping, etc.), etc. The front skirt of the hole is cracked;


Sixth, the back water is cracked: the cabinet is not flat or the pad is not flat;


Seventh, the back water side connection table surface cracking: glue bonding is not strong;


Eighth, the center of the countertop is cracked, etc.: subject to high temperature, impact by

 external force, cabinet or pad is not flat, the plate has internal injuries, etc.; therefore, the main

 factor causing the cracking of the countertop is caused by the poor quality control of the counterto

p during the processing.


Now, you can follow our website by scanning the code on your mobile phone.